Trilubgrease KXS–EP 792-550
Trilubgrease KXS-EP 792-550 is a mineral based, new generation, multi purpose Calcium Sulfonate Complex grease for heavy duty and high temperature having a long operation life and performance. Its resistance to water is high and shows long life performance between operating temperatures –20 and 300°C, in wet conditions and under varying, vibrant impact loads.
APPLICATION PLACES
- Cooling and transfer rolls
- Low and mid speed bearings, moving beds at high temperatures and under vibrant impact loads in rolling mills.
- Automotive applications, paper , mining, cement industries, agricultural and constructional machinery
- Moving band conveyor bearings working under heavy conditions
- Crane machinery
- Marine applications
NOTE: NOT mixable with sodium, calcium, and barium greases!
BENEFITS
- High performance even under heavy loads owing to high EP additives.
- Very high dropping point and thus high operating temperature.
- Very good resistance to water, protects the bearings under muddy and heavy conditions.
- Keeps its consistency even after long operation.
- Absorbs vibrant impact loads and decreases friction and wear.
- Very good corrosion protection through antioxidant and anticorrosion additives.
- Decreases maintenance and operating costs by increasing the life of the bearings.
- Can be easily used in central lubrication systems thanks to the NLGI stability.
PACKAGES : 16 Kg, 180 Kg
PROPERTIES
| Trilubgrease KXS-EP | Standart | 792-550 |
| NLGI | DIN 51818 | 2 |
| Color | Red | |
| Base Oil | Mineral | |
| Soap Type | Calsium sulfonate complex | |
| Worked penetration 60 ST, 25 °C | ASTM D 217 | 285 |
| İşWorked penetration 100.000 ST, 25 °C | ASTM D 217 | 300 |
| Density 20 °C , g/cm3 | DIN 51757 | ~ 0,91 |
| Base Oil viscosity, 40 °C mm2/sec | ISO VG | 550 |
| Dropping point, [°C] | DIN ISO 2176 | > 400 |
| Oil seperation amount [ % Weight ] 40 °C , 42 h | FTMS 791 C 321.3 | 0,5 Max. |
| Copper Corrosion, 24 h/100 °C | DIN 51811 | Max. 1 b |
| Timken OK Load (lbs) | ASTM D2509 | 45 min |
| Shell 4 ball test , Weld load (kg) | ASTM D 2596 | 400 |
|
Shell 4 ball test. Wear – Scar diameter (mm) 1800 rpm, 60kg, 60 sec,
25 °C.
|
IP 239 | 0,6 max |
| Antioxidant property 100C, 100 hrs. Reduction in pressure(kg/cm3) | 0,25 | |
| Water test , %Weight | ASTM D 4049 | 3 max. |
| Oxidation stability (psi ), 100 h | ASTM D 942 | 10 max. |
| Copper test | ASTM D 1743 | Ok |
| Speed factor ( nxdm ) | d+D/2 x n | 400.000 |
(*) given values are typical and may vary in production.
Warning: The explanations and technical values in this document are general data which are obtained by research and experience. Our company do not accept any responsibility in case of any damage caused by wrong application of lubricants or wrong lubricant choice. Please consult technical experts for the right choice of lubricant and application.