Trilubgrease MS 692
Trilubgrease MS 692 is a black greases; strengthened with Molybdenum Disulphite, containing mineral base oil and Lithium soap with a wide range of applications.
Shows high performance even under shock and variable loads between the operating temperatures –20 and 160 °C.
APPLICATION PLACES
- Fan and electric motor bearings
- Automotive, paper, mining, cement, agricultural machinery, construction equipment.
- Water pumps,
- Generators,
- Conveyor beds with moving bands
- Crane mechanisms,
- Taret lubrication,
- Automobile and railway vehiche axle bearings.
BENEFITS
- Shows high performance thanks to its molybdenum sulphite compound.
- Damps vibrating and shock loads, decreases friction and wear.
- Can be applied easily with grease gun, brush or spatula.
- Protects bearings against water and provides leak proof.
- Excellent protection from corrosion and oxidation
- By increasing service life of bearings it decreases maintenance costs.
PACKAGES : 1 Kg, 16 Kg, 180 Kg
PROPERTIES
| Trilubgrease MS | Standart | 692 |
| NLGI | DIN 51818 | 2 |
| Color | Black | |
| Base Oil | Mineral | |
|
Dry Lubricating EP additive MoS2 ,( % Weight )
|
3 | |
| Soap Type | Lithium | |
| Worked penetration 60 ST, 25 °C | ASTM D 217 | 265 – 295 |
| Density 20 °C , g/cm3 | DIN 51757 | 0,92 |
| Base Oil viscosity, 40 °C mm2/sec | ISO VG | 550 |
| Soap Amount [ % Weight ] | 10 – 11 | |
| Dropping point, [°C] | DIN ISO 2176 | 195 Min. |
| Alkality: mg KOH / mg | 1 Max. | |
|
Oil seperation amount [ % Weight ] , 40 °C , 42 h
|
IP 121 | 5, 0 Max |
| Copper Corrosion, 24 h/100 °C | DIN 51811 | Max. 1 b |
| Speed factor ( nxdm ) | 300.000 |
(*) given values are typical and may vary in production.
Warning: The explanations and technical values in this document are general data which are obtained by research and experience. Our company do not accept any responsibility in case of any damage caused by wrong application of lubricants or wrong lubricant choice. Please consult technical experts for the right choice of lubricant and application.