Trilubgrease LXA–EP 692-220
Trilubgrease LXA-EP 692-220 is a high performance, strengthened by high quality Extreme Pressure (EP) additive, Lithium complex soap developed for heavy conditions and high temperatures.  Resistance to water is enhanced by Aluminum Stearat.
 
Trilubgrease LXA-EP 692-220 shows high performance even under  shock, variable vibrational loads with water between the operating temperatures –20 and 180 °C 
 
APPLICATION PLACES
  • In iron-steel industry, bearings and moving beds which work under vibration, shock load and high temperature with middle and high rpm.
  • Automotive, paper, mining, cement, agricultural machinery and construction equipment industries,
  • Fan and electric motor bearings,
  • Generators, 
  • Moving band conveyor beds working under heavy conditions.
  • Crane mechanisms,
  • Taret lubrication,
  • Suitable for marine applications.
 
BENEFITS
  • Thanks to Extreme Pressure (EP) additives it shows high performance even under hevy loads and high temperatures.
  • Damps vibration and shock load, decreases friction and wear.
  • Protection for bearings under heavy conditions, water, and mud. Also provides leakproof.
  • Excellent protection from corrosion and oxidation. 
  • By increasing service life of bearings it decreases maintenance costs. 
  • Due to its NLGI stability Trilubgrease LXA-EP 692-220 can be used in central lubrication system without any problem.
 
PACKAGES : 16 Kg, 180 Kg

 

PROPERTIES

Trilubgrease LXA - EP Standart 692 - 220
NLGI DIN 51818 2
Color    Blue
Base Oil    Mineral
Soap Type   
Lithium Complex ,
 Aluminium soap
Worked penetration 60 ST,  25 °C  ASTM D 217 265-295
Density  20 °C , g/cm3 DIN 51757 ~0,92
Base Oil viscosity, 40 °C  mm2/sec  ISO VG  220
Soap Amount [ % Weight ]    10-13
Dropping point, [°C] DIN ISO 2176 > 290
Oil seperation amount  [ % Weight ]   40 °C , 42 h    FTMS 791 C  4, 0 Max.
Copper Corrosion,  24 h/100 °C DIN 51811 Max. 1 a
Timken OK Load (lbs) ASTM D2509 35 min
Shell 4 ball test , Weld load (kg) ASTM D 2596 > 815
Shell 4 ball test. Wear – Scar diameter (mm) 1800 rpm, 60kg, 60 sec, 25 °C.  IP 239 0,5 max
Antioxidant property 100C, 100 hrs. Reduction in pressure(kg/cm3)   0,25
Water test , %Weight ASTM D 4049 6 max.
Copper test ASTM D 1743 Ok
Speed factor ( nxdm ) d+D/2 x n 400.000

 

(*) given values are typical and may vary in production.
 
Warning: The explanations and technical values in this document are general data which are obtained by research and experience. Our company  do not accept any responsibility in case of any damage caused by wrong application of lubricants or wrong lubricant choice. Please consult technical experts for the right choice of lubricant and application.