Trilubgrease LXN–EP 692-110
Trilubgrease LXN-EP 692-110 is a high performance, strengthened by high quality Extreme Pressure (EP) additive, new age Lithium complex soap developed for heavy conditions and high temperatures.  
Trilubgrease LXN-EP 692-110 shows high performance even under  shock, variable vibrational loads with water between the operating temperatures –20 and 220 °C 
  • In iron-steel industry, bearings and moving beds which work under vibration, shock load and high temperature with middle and high rpm.
  • Automotive, paper, mining, cement, agricultural machinery and construction equipment industries,
  • Moving band conveyor beds working under heavy conditions.
  • Crane mechanisms,
  • Suitable for marine applications.
  • Thanks to Extreme Pressure (EP) additives it shows high performance even under hevy loads and high temperatures.
  • Damps vibration and shock load, decreases friction and wear.
  • Protection for bearings under heavy conditions, water, and mud. Also provides leakproof.
  • Excellent protection from corrosion and oxidation. 
  • By increasing service life of bearings it decreases maintenance costs. 
  • Due to its NLGI stability Trilubgrease LXN-EP 692-110 can be used in central lubrication system without any problem.
PACKAGES : 16 Kg, 180 Kg



Trilubgrease LXN-EP Standart 692-110
NLGI DIN 51818 1
Color   Blue
Base Oil    Mineral
Soap Type    Special Lithium Complex
Worked penetration 60 ST,  25 °C  ASTM D 217 265 - 295
Density  20 °C , g/cm3 DIN 51757 ~0,91
Base Oil viscosity, 40 °C  mm2/sec  ISO VG  100-120
Soap Amount [ % Weight ]    15,5– 16
Dropping point, [°C] DIN ISO  2176 > 312
Oil seperation amount , [ % Weight ]   40 °C , 42 h    FTMS 791 C  5.0 Max
Copper Corrosion, 24 h/100 °C DIN 51811 Max. 1 b
Timken OK Load (lbs) ASTM D2509 35 min
Shell 4 ball test , Weld load (kg) ASTM D 2596 > 450
Shell 4 ball test. Wear – Scar diameter (mm) 1800 rpm, 60kg, 60 sec, 25 °C. IP 239 0,5 max
Antioxidant property 100°C, 100 hrs. Reduction in pressure(kg/cm3)   0,25
Water test , %Weight ASTM D 4049 6 max.
Oxidation stability  (psi ), 100 h ASTM D 942 10 max.
Copper test ASTM D 1743 Ok
Speed factor ( nxdm ) d+D/2 x n 550.000


(*) given values are typical and may vary in production.
Warning: The explanations and technical values in this document are general data which are obtained by research and experience. Our company  do not accept any responsibility in case of any damage caused by wrong application of lubricants or wrong lubricant choice. Please consult technical experts for the right choice of lubricant and application.