Trilubgrease LXN–MSG 692-220
Trilubgrease  LXN-MSG 692-220 is a mineral based high performance special lithium-lithium complex grease with  graphite and MoS2 additives for heavy duty and high temperatures.
Trilubgrease LX - MSG 692-220 shows high performance even under  shock, variable vibration loads with water between operating temperatures –20°C and 210°C.
  • Rotary kiln in cement industries where high temperature and dusty conditions are present
  • Middle and high rpm bearings in iron-steel industry
  • Automotive, paper, mining, cement, agricultural machinery, construction equipment
  • Fan and electric motor bearings
  • Generators
  • Heavy duty moving band conveyor beds
  • Crane mechanism
  • Turret lubrication
  • Suitable for marine applications
NOTE: NOT mixable with sodium, calcium and barium greases!
  • Thanks to Molybdenum Sulphite and Graphite Compound, shows high performance even under heavy conditions and high temperature.
  • Damps vibration and shock load, decreases friction and wear.
  • Protection for bearings under heavy conditions, water, and mud. Also provides leak proof.
  • Excellent protection from corrosion and oxidation. 
  • By increasing service life of bearings it decreases maintenance costs. 
  • Owing to its NLGI stability Trilubgrease LXN-MSG 692-220 can be used in central lubrication systems without any problem.
PACKAGES : 16 Kg, 180 Kg


Trilubgrease LXN-MSG Standart 692-220
NLGI DIN 51818 2
Color   Black
Base Oil    Mineral
Soap Type    Li -Complex
Worked penetration 60 ST, 25 °C  ASTM D 217 265 - 295
Density  20 °C , g/cm3 DIN 51757 ~0,91
Base Oil viscosity, 40 °C  mm2/sec  ISO VG  220
Soap Amount [ % Weight ]    15,3 – 15,6
Dropping point, [°C] DIN ISO  2176 > 320
Oil seperation amount [ % Weight ] ,  150°C , 30 h    IP 121 1, 4 Max.
Copper Corrosion, 24 h/100 °C DIN 51811 Max. 1 b
Timken OK Load (lbs) ASTM D2509-68 12
Shell 4 ball test , Weld load (kg) ASTM D 2596 > 500
Shell 4 ball test. Wear – Scar diameter (mm) 1800 rpm, 60kg,  60 sec, 25 °C.  IP 239 0,54
Antioxidant property 100C, 100 hrs. Reduction in pressure(kg/cm3)   0,25
Speed factor ( nxdm ) d+D/2 x n 400.000


(*) given values are typical and may vary in production.
Warning: The explanations and technical values in this document are general data which are obtained by research and experience. Our company  do not accept any responsibility in case of any damage caused by wrong application of lubricants or wrong lubricant choice. Please consult technical experts for the right choice of lubricant and application.