Trilubgrease Temp LX–MSG 692-460
Trilubgrease Temp LX-MSG 692-460  is a high performance grease for heavy duty and high temperature applications. Produced with graphite and MoS2, mineral base oil, Lithium- Lithium complex soap.
Trilubgrease Temp LX-MSG 692-460 shows high performance even under  shock, variable vibration loads with water between the operating temperatures –20 and 180 °C
 
APPLICATION PLACES
  • Rotary Kiln in cement industries where high temperature and dusty conditions are present.
  • Middle and high rpm bearings in iron-steel industry.
  • Automotive, paper, mining, cement, agricultural machinery, construction equipments,
  • Fan and electric motor bearings.
  • Generators, 
  • Heavy duty moving band conveyor beds.
  • Crane mechanism,
  • Taret lubrication,
  • Suitable for marine applications.
 
BENEFITS
  • Thanks to Molybdenum Sulphite and Graphite Compound, shows high performance even under heavy conditions and high temperature.
  • Damps vibration and shock load, decreases friction and wear.
  • Protection for bearings under heavy conditions, water, and mud. Also provides leak proof.
  • Excellent protection from corrosion and oxidation. 
  • By increasing service life of bearings it decreases maintenance costs. 
  • Due to its NLGI stability Trilubgrease Temp LX-MSG 692-460 can be used in central lubrication system without any problem.
 
PACKAGES : 16 Kg, 180 Kg

PROPERTIES

Trilubgrease Temp LX-MSG Standart 692-460
NLGI DIN 51818 2
Color   Black
Base Oil    Mineral
Soap Type    Lithium Complex
Worked penetration 60 ST, 25 °C  ASTM D 217 265 - 295
Density  20 °C , g/cm3 DIN 51757 ~0,92
Base Oil viscosity, 40 °C  mm2/sec  ISO VG  460
Soap Amount [ % Weight ]    8 - 10
Dropping point, [°C] DIN ISO  2176 > 290
Oil seperation amount [ % Weight ] ,  40 °C , 42 h    IP 121 5,0 Max
Copper Corrosion, 24 h/100 °C DIN 51811 Max. 1 b
Timken OK Load (lbs) ASTM D2509-68 12
Shell 4 ball test , Weld load (kg) ASTM D 2596 > 500
Shell 4 ball test. Wear – Scar diameter (mm) 1800 rpm, 60kg, 60 sec, 25 °C.  IP 239 0,538
Antioxidant property 100C, 100 hrs. Reduction in pressure(kg/cm3)   0,25
Speed factor ( nxdm ) d+D/2 x n 300.000

 

(*) given values are typical and may vary in production.
 
Warning: The explanations and technical values in this document are general data which are obtained by research and experience. Our company  do not accept any responsibility in case of any damage caused by wrong application of lubricants or wrong lubricant choice. Please consult technical experts for the right choice of lubricant and application.